Categories | High Alumina Refractory Brick |
---|---|
Brand Name: | Rongsheng |
Certification: | CE/ISO9001 |
Place of Origin: | China Henan Province |
MOQ: | 5 TONS |
Price: | USD 250-400 |
Supply Ability: | 3000 TONS PER MONTH |
Delivery Time: | 10-15 WORKING DAYS |
Packaging Details: | PALLET PACKING STANDARD EXPORT PACKING |
Payment Terms: | T/T, Western Union, MoneyGram |
Material: | Bauxite Chamotte |
Al₂O₃: | ≥55 |
Shape: | standard size or customized |
Bulk Density: | 2.2 g/cm³ |
Apparent porosity: | 20-23 % |
Cold crushing strength: | 45 MPa |
Refractoriness under load, 0.2MPa: | 1450 °C |
Company Info. |
Zhengzhou Rongsheng Refractory Co., Ltd. |
Verified Supplier |
View Contact Details |
Product List |
General Industrial Furnace Bricks , Insulating Fire Brick High Temperature
High Alumina Bricks are produced with selected bauxite chamotte as
main raw material, fired at 1450-1470 °C by advanced process with
strict quality control.
High Alumina bricks have great features like high temperature
performance, great corrosion and wear resistance, high bulk
density, low iron content, etc. High Alumina bricks are extensively
used in mining, metallurgy, cement, chemical and refinery and
refractory industries.
These bricks are used in all kinds of industrial furnace and high
temperature areas to prolong the lives of furnaces.
Index | Item | ||||
LZ-75 | LZ-65 | LZ-55 | LZ-48 | ||
Al2O3 ,%≥ | 75 | 65 | 55 | 48 | |
Refractoriness, ℃≤ | 1790 | 1770 | 1750 | ||
0.2Mpa refractoriness under load, ℃≤ | 1520 | 1500 | 1470 | 1420 | |
Reheating linear change, % | 1500℃,2h | +0.1 -0.4 | - | ||
1450℃,2h | - | +0.1 -0.4 | |||
Apparent porosity, %≤ | 23 | 22 | |||
Compress strength, MPa≥ | 53.9 | 49.0 | 44.1 | 39.2 |
High Alumina Bricks,their typical properties include high refractoriness, crushing strenght, density, abrasion resistence and with increased resistence to molten metals, slags, glass and other chemici impacts. They are used to walls, rous and extremely stress parts of metalurgy aggregates (hot blast stoves, blast pipes, gorn of blast furnaces, torpedo ladles and pouring ladles for raw metal, casting ladles), shaft and rotary furnaces for firing lime and cement, linings of tunnel fonace of firing ceramics, turner blocks and ceramics burners' endings.
HIGH-ALUMINA BRICK FOR ELECTRICAL ARCH FURNACE
Item | Al2O3 | Refractory ℃ | A.P. | C.C.S | R.U.L 0.2 ℃ | P.L.C |
DL-80 | ≥80% | ≥1790 | ≥19% | ≥78.5 | ≥1530 | 0-0.3 |
DL-75 | ≥75% | ≥1790 | ≥19% | ≥68.6 | ≥1530 | 0-0.4 |
HIGH-ALUMINA BRICK FOR BLAST FURNACE
Item | Al2O3 | Fe2O3 | A.P. | C.C.S | R.U.L 0.2 °C | P.L.C |
GL-65 | ≥65% | ≥2.0% | ≥19% | ≥58.8 | ≥1500 | 0-0.2 |
GL-55 | ≥55% | ≥2.0% | ≥19% | ≥49.0 | ≥1480 | 0-0.2 |
THERMAL SHOCK RESISTANCE HIGH-ALUMINA BRICKS
Item | Al2O3 | Zr2O | A.P. | B.D. g/cm3 | C.C.S | R.U.L 0.2 °C | T.S.R (water cycle) 1100°C |
KBLZ-75 | ≥75% | 5-7% | ≥23% | ≥2.60 | ≥50.0 | ≥1500 | ≥20 |
KBLZ-70 | ≥70% | 5-7% | ≥25% | ≥2.55 | ≥45.0 | ≥1470 | ≥20 |
LOW GREEP HIGH-ALUMINA BRICKS
Item | Al2O3 | A.P. | C.C.S | P.L.C |
DRLZ-80 | ≥85% | ≥20% | ≥60.0 | (1550°C)0.8% |